 PET Film(Metallizing application) |
|
|
 FM00
12MIC |
|
| PROPERTY |
UNIT |
STANDARD |
TEST METHOD |
TENSILE
STRENGTH |
MD |
kg / ㎟ |
27.0±3.0 |
ASTM D-882 |
| TD |
27.0±3.0 |
ELONGATION
(AT BREAK) |
MD |
% |
120.0±25.0 |
ASTM D-882 |
| TD |
130.0±25.0 |
F - 5
VALUE |
MD |
kg / ㎟ |
12.0±1.0 |
ASTM D-882 |
| TD |
11.0±1.0 |
HEAT-SHRINKAGE
(IN HOT AIR) |
MD |
% |
1.4±0.3 |
(150℃, 30min) |
| TD |
0.0±0.2 |
| MD |
4.2±0.3 |
(200℃, 10min) |
| TD |
0.4±0.3 |
FRICTION
COEFFICIENT
(FILM/FILM) |
uS |
|
0.33±0.05 |
ASTM D-1894 |
| uK |
0.36±0.05 |
| HAZE |
% |
2.2±0.5 |
ASTM D-1003 |
|
| FS01
23MIC |
|
| PROPERTY |
METRIC(S.I.)UNITS |
TEST METHOD |
| UNIT |
TYPICAL VALUE |
AVERAGE
THICKNESS |
㎛ |
23 |
|
| YIELD |
m²/ kg |
31.06 |
|
TENSILE
STRENGTH |
MD
TD |
kg / ㎟
kg / ㎟ |
30
24 |
ASTM
D-882 |
ELONGATION
AT BREAK |
MD
TD |
%
% |
135
165 |
ASTM
D-882 |
F - 5
VALUE |
MD
TD |
kg / ㎟
kg / ㎟ |
13
11 |
ASTM
D-882 |
HEAT-SHRINKAGE
(10min, 200℃) |
MD
TD |
%
% |
4.5
0.2 |
ASTM
D-2305 |
FRICTION
COEFFICIENT |
uS
uK |
|
0.27
0.37 |
ASTM
D-1894 |
WETTING
TENSION |
IN
OUT |
dyne/cm
dyne/cm |
52
40 |
ASTM
D-2578 |
HAZE
FF |
|
%
FF |
1.2
DK |
ASTM
D-1003 |
| TEST CONTDITION |
Normal laboratory condition : 23℃, 50%RH |
|
 |
| FS01
50MIC |
|
| PROPERTY |
METRIC(S.I.)UNITS |
TEST METHOD |
| UNIT |
TYPICAL VALUE |
AVERAGE
THICKNESS |
㎛ |
50 |
|
| YIELD |
m²/ kg |
14.29 |
|
TENSILE
STRENGTH |
MD
TD |
kg / ㎟
kg / ㎟ |
20
22 |
ASTM
D-882 |
ELONGATION
AT BREAK |
MD
TD |
%
% |
180
135 |
ASTM
D-882 |
F - 5
VALUE |
MD
TD |
kg / ㎟
kg / ㎟ |
12
11 |
ASTM
D-882 |
HEAT-SHRINKAGE
(10min, 200℃) |
MD
TD |
%
% |
2.2
0.5 |
ASTM
D-2305 |
FRICTION
COEFFICIENT |
uS
uK |
|
0.30
0.35 |
ASTM
D-1894 |
WETTING
TENSION |
IN
OUT |
dyne/cm
dyne/cm |
52
40 |
ASTM
D-2578 |
HAZE
FF |
|
%
FF |
0.7
DK |
ASTM
D-1003 |
| TEST CONTDITION |
Normal laboratory condition : 23℃, 50%RH |
|
|