 Black PET Film |
|
|
 |
 SB00 |
It
is a black polyester film with low contents of carbon black. It has high
optical density,
so light can hardly be transmitted through. And it has
no large surface protrusion.
It is applicable in various industrial applications
including cable wrapping jacket, speeker vibrator, and
ETC. It is available in the thickness ranging from 12μ
up to 188μ. |
 |
 SB00 12MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
48 |
|
| (㎛) |
(12) |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
28,400 (20.0) |
ASTM D-882
|
| TD |
37,000 (26.0) |
ELONGATION
(AT BREAK) |
MD |
% |
168 |
ASTM D-882
|
| TD
|
127 |
| Friction Coefficient |
μk |
|
0.29 |
ASTM D-1894 |
| μs |
0.37 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
1.0 X 10 |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
113 |
ASTM D-623 |
| Light Transmission |
% |
13.0 |
ASTM D-1003 |
| Optical Density |
|
0.89 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.1 |
150℃, 30min |
| TD |
0.0 |
|
* Unit Correlation : Gauge = ㎛/0.264
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 9.8
 |
| SB00 16MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
64 |
|
| (㎛) |
(16) |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
27,000 (20) |
ASTM D-882
|
| TD |
34,100 (24) |
ELONGATION
(AT BREAK) |
MD |
% |
175 |
ASTM D-882
|
| TD
|
112 |
| Friction Coefficient |
μk |
|
0.29 |
ASTM D-1894 |
| μs |
0.39 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
2.2 X 10¹⁴ |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
117 |
ASTM D-523 |
| Light Transmission |
% |
10.0 |
ASTM D-1003 |
| Optical Density |
|
1.0 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.3 |
150℃, 30min |
| TD |
0.0 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 25MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
100 |
|
| (㎛) |
25.0 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
28,400 (20) |
ASTM D-882
|
| TD |
35,600 (25) |
ELONGATION
(AT BREAK) |
MD |
% |
148 |
ASTM D-882
|
| TD
|
127 |
| Friction Coefficient |
μk |
|
0.24 |
ASTM D-1894 |
| μs |
0.31 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
2.4 X 10¹⁴ |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
100 |
ASTM D-523 |
| Light Transmission |
% |
2.0 |
ASTM D-1003 |
| Optical Density |
|
1.83 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
2.5 |
190℃, 30min |
| TD |
0.3 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 38MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
160 |
|
| (㎛) |
38.0 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
28,400 (20) |
ASTM D-882
|
| TD |
34,100 (24) |
ELONGATION
(AT BREAK) |
MD |
% |
168 |
ASTM D-882
|
| TD
|
143 |
| Friction Coefficient |
μk |
|
0.25 |
ASTM D-1894 |
| μs |
0.30 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
7.3 X 10¹² |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
100 |
ASTM D-523 |
| Light Transmission |
% |
0.3 |
ASTM D-1003 |
| Optical Density |
|
2.52 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
2.2 |
190℃ X 20min |
| TD |
0.3 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 50MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
200 |
|
| (㎛) |
50 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
27,000 (19) |
ASTM D-882
|
| TD |
32,700 (23) |
ELONGATION
(AT BREAK) |
MD |
% |
220 |
ASTM D-882
|
| TD
|
110 |
| Friction Coefficient |
μk |
|
0.32 |
ASTM D-1894 |
| μs |
0.42 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
1.0 X 10¹⁴ |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
110 |
ASTM D-523 |
| Light Transmission |
% |
0.0 |
ASTM D-1003 |
| Optical Density |
|
3.16 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.4 |
150℃, 30min |
| TD |
0.2 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 75MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
300 |
|
| (㎛) |
75 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
27,000 (19) |
ASTM D-882
|
| TD |
34,100 (24) |
ELONGATION
(AT BREAK) |
MD |
% |
221 |
ASTM D-882
|
| TD
|
109 |
| Friction Coefficient |
μk |
|
0.32 |
ASTM D-1894 |
| μs |
0.44 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
1.0 X 10¹⁴ |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
110 |
ASTM D-523 |
| Light Transmission |
% |
0.0 |
ASTM D-1003 |
| Optical Density |
|
4.38 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.5 |
150℃, 30min |
| TD |
0.2 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 100MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
400 |
|
| (㎛) |
100 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
29,900 (21) |
ASTM D-882
|
| TD |
32,700 (23) |
ELONGATION
(AT BREAK) |
MD |
% |
206 |
ASTM D-882
|
| TD
|
114 |
| Friction Coefficient |
μk |
|
0.38 |
ASTM D-1894 |
| μs |
0.53 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
1.0 X 10¹⁴ |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
110 |
ASTM D-523 |
| Light Transmission |
% |
0.0 |
ASTM D-1003 |
| Optical Density |
|
4.7 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.7 |
150℃, 30min |
| TD |
0.0 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 125MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
500 |
|
| (㎛) |
125 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
28,400 (20) |
ASTM D-882
|
| TD |
32,700 (23) |
ELONGATION
(AT BREAK) |
MD |
% |
206 |
ASTM D-882
|
| TD
|
113 |
| Friction Coefficient |
μk |
|
0.32 |
ASTM D-1894 |
| μs |
0.44 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
1.0 X 10¹⁴ |
ASTM D 257 |
| OPTICAL |
| Gloss |
% |
100 |
ASTM D-523 |
| Light Transmission |
% |
0.0 |
ASTM D-1003 |
| Optical Density |
|
4.7 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.7 |
150℃, 30min |
| TD |
0.0 |
|
* Unit Correlation : Gauge = ㎛/0.254
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 8.8
|
| SB00 188MIC |
|
| PROPERTY |
UNIT |
VALUE |
TEST METHOD |
| GENERAL |
| NORMINAL THICKNESS
|
Gauge |
740 |
|
| (㎛) |
188 |
| MECHANICAL |
| TENSILE STRENGTH
|
MD |
psi
(kg / ㎟) |
24,200 (17.0) |
ASTM D-882
|
| TD |
24,200 (17.0) |
ELONGATION
(AT BREAK) |
MD |
% |
205 |
ASTM D-882
|
| TD
|
152 |
| Friction Coefficient |
μk |
|
0.32 |
ASTM D-1894 |
| μs |
0.35 |
| Electrical |
| Surface Resistance |
|
Ω/□ |
1.0 X 10 |
NFPA 58A |
| OPTICAL |
| Gloss |
% |
100 |
ASTM D-523 |
| Light Transmission |
% |
0 |
ASTM D-1003 |
| Optical Density |
|
4.9 |
|
| THERMAL |
HEAT
Shrinkage |
MD |
% |
1.5 |
150℃, 30min |
| TD |
0.4 |
|
* Unit Correlation : Gauge = ㎛/0.264
psi = Kg/㎟ x 1422.3
N/㎟ = Kg/㎟ x 9.8
|